Facile synthesis of monodisperse Cu3SbSe4 nanoparticles and thermoelectric performance of Cu3SbSe4 nanoparticle-based materials - Université de Rennes Accéder directement au contenu
Article Dans Une Revue Journal of Nanoparticle Research Année : 2015

Facile synthesis of monodisperse Cu3SbSe4 nanoparticles and thermoelectric performance of Cu3SbSe4 nanoparticle-based materials

Résumé

In this study, large-scale synthesis of Cu3SbSe4 and Cu3Sb0.98Sn0.02Se4 nanoparticles with a narrow size distribution was achieved through a rapid-injection route. These nanoparticles showed a monodisperse and quasi-spherical morphology. The Cu3SbSe4 and Cu3Sb0.98Sn0.02Se4 nanoparticle-based bulk materials were then prepared by hot-pressed sinter of the nanoparticles, and their thermoelectric performances were systematically studied. Due to the reduced lattice thermal conductivity from enhanced phonon scattering at the grain interfaces of the bulk materials, the maximum ZT value of the Cu3Sb0.98Sn0.02Se4 bulk materials reached 0.50 at 575 K
Fichier principal
Vignette du fichier
Facile synthesis of monodisperse Cu3SbSe4 nanoparticles - revised.pdf (245.41 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01174904 , version 1 (16-09-2015)

Identifiants

Citer

Yimin Wu, Xvsheng Qiao, Xianping Fan, Xianghua Zhang, Shuo Cui, et al.. Facile synthesis of monodisperse Cu3SbSe4 nanoparticles and thermoelectric performance of Cu3SbSe4 nanoparticle-based materials. Journal of Nanoparticle Research, 2015, 17 (7), In press. ⟨10.1007/s11051-015-3094-2⟩. ⟨hal-01174904⟩
130 Consultations
218 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More