Dy3+ doped GaGeSbSe fiber long-wave infrared emission - Université de Rennes Accéder directement au contenu
Article Dans Une Revue Journal of Luminescence Année : 2020

Dy3+ doped GaGeSbSe fiber long-wave infrared emission

Résumé

We report on the mid-wave infrared (MWIR) and long-wave infrared (LWIR) emissions of a 1000 ppm Dy 3+ doped Ga 5 Ge 20 Sb 10 Se 65 chalcogenide fiber. Following a shortwave infrared (SWIR) optical pumping at 0.92, 1.12 and 1.32 µm using commercial laser diodes, LWIR luminescence around 7.3 µm (6 H 7/2 → 6 H 9/2 transition) was recorded for the first time to the best of our knowledge along with MWIR emissions around 4.3 µm and 5.4 µm with a Dy 3+ doped Ga 5 Ge 20 Sb 10 Se 65 fiber. Frequency dependent spectroscopic investigation clearly shows that this LWIR luminescence originates from the 6 H 7/2 manifold. Spectroscopic properties of this Dy 3+ doped material and the comparison with its equivalent sulfide Dy 3+ :Ga 5 Ge 20 Sb 10 S 65 glass are presented.
Fichier principal
Vignette du fichier
JLum Dy LWIR SUBMIT.pdf (602.95 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03100227 , version 1 (06-01-2021)

Identifiants

Citer

F. Starecki, G. Louvet, J. Ari, A. Braud, Jean-Louis Doualan, et al.. Dy3+ doped GaGeSbSe fiber long-wave infrared emission. Journal of Luminescence, 2020, 218, pp.116853. ⟨10.1016/j.jlumin.2019.116853⟩. ⟨hal-03100227⟩
107 Consultations
122 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More