Influence of precipitate/supernatant ratio during liquid-phase synthesis of solid electrolyte Li7P3S11

Bo Fan
  • Fonction : Auteur
Xianghua Zhang
Hongli Ma
Ping Fan
  • Fonction : Auteur
Bai Xue
Connectez-vous pour contacter l'auteur

Résumé

Delicate control of the precipitate/supernatant ratio in the precursor suspension during liquid-phase synthesis of Li7P3S11 provides information on how the morphology of the impurities affect the ionic conductivity. In this work, the influence of the precipitate/supernatant ratio on the phase structure, the morphology and the ionic conductivity of Li7P3S11 prepared in acetonitrile is studied. It is revealed that in the supernatant-excess region, the excess amorphous "Li2S·P2S5" finally turns into a poorly ionic conductive phase Li4P2S6 which wraps Li7P3S11 particles, increasing the interfacial resistance. In the precipitate-excess region, a thio-LISICON III phase turned from the excess precipitate tends to stay within Li7P3S11 particles, and therefore its negative influence on the total ionic conductivity is not evident. Consequently, a slight composition shift into the precipitate-excess region benefits the ionic conductivity of the resultant solid electrolyte.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Xu_et al_2019_Influence of precipitate supernatant ratio_accepted.pdf (1.95 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02367902 , version 1 (30-03-2020)

Identifiants

Citer

Bo Fan, Quanfeng Zhang, Zhongkuan Luo, Xianghua Zhang, Hongli Ma, et al.. Influence of precipitate/supernatant ratio during liquid-phase synthesis of solid electrolyte Li7P3S11. Solid State Ionics, 2019, 343, pp.115073. ⟨10.1016/j.ssi.2019.115073⟩. ⟨hal-02367902⟩
26 Consultations
343 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More