Fissuring and Fragmentation Removal During Sol-Gel Catalytic Materials Synthesis: An Experimental Design Approach - Université de Rennes Accéder directement au contenu
Article Dans Une Revue Journal of Sol-Gel Science and Technology Année : 2005

Fissuring and Fragmentation Removal During Sol-Gel Catalytic Materials Synthesis: An Experimental Design Approach

Résumé

Statistical designs were used to investigate the effects of various processing conditions on the fissuring and/or fragmentation of sol-gel catalytic materials. Three types of sol-gel materials were studied: SiO 2 , TiO 2-doped SiO 2 and CeO 2-doped SiO 2. Five processing variables were investigated: the quantity of water included in the sol-gel preparation, the amount of TiO 2 or CeO 2 precursors, the mixing time, the gelation time and the influence of treatment in an oven at 40 • C prior to the heating treatment (pre-heating time). Processing variables were set at high and low limits in three different 2 4 full-factorial designs. As notable results, the water content appeared to be a critical processing variable in every studied factorial designs. Pre-heating time was also significant for SiO 2 gels. Finally the amount of CeO 2 precursor and the gelation time were found to be influential for the synthesis of non-cracked CeO 2-doped SiO 2 sol-gel monoliths.

Domaines

Catalyse Matériaux
Fichier principal
Vignette du fichier
Raillardjsgst2005versionHAL.pdf (335.92 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02362982 , version 1 (18-11-2019)

Identifiants

Citer

C. Raillard, Valérie Hequet, P. Le Cloirec, J. Legrand. Fissuring and Fragmentation Removal During Sol-Gel Catalytic Materials Synthesis: An Experimental Design Approach. Journal of Sol-Gel Science and Technology, 2005, 34 (1), pp.5-14. ⟨10.1007/s10971-005-1257-9⟩. ⟨hal-02362982⟩
30 Consultations
78 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More