Microhardness and optical property of chalcogenide glasses and glass‐ceramics of the Sn–Sb–Se ternary system

Abstract

The microhardness of chalcogenide glasses (ChGs) of the Sn–Sb–Se (SSS) ternary system was investigated, and the correlation of microhardness with the mean coordination number of the SSS ChGs was determined. To prepare infrared‐transparent SSS glass‐ceramics (GCs), two SSS ChGs (A, Sn6.23Sb14.11Se79.66; B, Sn9.8Sb17.22Se72.98; by molar composition) were selected and thermally treated at 433 and 448 K, respectively. The improved microhardness (with values that increased by 11.5% and 7.3% for SSS ChG A and B, respectively) of the resulting SSS GCs is attributed to the formation of Sb2Se3 nanocrystals.
Fichier principal
Vignette du fichier
Xue et al. - Microhardness and optical property of chalcogenide.pdf (729.55 Ko) Télécharger le fichier
Origin : Files produced by the author(s)
Loading...

Dates and versions

hal-01952379 , version 1 (12-12-2018)

Identifiers

Cite

Xuning Xue, Feifei Chen, Changgui Lin, Ruiqiang Lin, Xiaoyu Zhang, et al.. Microhardness and optical property of chalcogenide glasses and glass‐ceramics of the Sn–Sb–Se ternary system. Journal of the American Ceramic Society, 2019, ⟨10.1111/jace.15980⟩. ⟨hal-01952379⟩
17 View
170 Download

Altmetric

Share

Gmail Facebook X LinkedIn More