Te-As-Se glass destabilization using high energy milling

Résumé

The Te 20 As 30 Se 50 (TAS) glass has been studied under the extreme conditions of high energy milling. Starting from the raw materials, an amorphization process occurs progressively reaching an unstable intermediate state and the final stable state then. Despite its high resistance against crystallization when made using silica tubes, an intermediate state is reached when mechanically alloyed into powder. The evolution of the glass structure has been investigated using Raman spectroscopy and MAS NMR of 77 Se according to the milling time. Optimized parameters and conditions to compact milled powders by Spark Plasma Sintering show the possibility to design infrared windows transparent from 2 to 20µm. A correlation to the thermo-mechanical properties of densified powder using hot pressing has been made.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Te-As-Se glass destabilization_accepted.pdf (1.07 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01660838 , version 1 (11-12-2017)

Identifiants

Citer

Laurent Calvez, Enora Lavanant, Anna Novikova, Claudia Gonçalves, Bruno Bureau, et al.. Te-As-Se glass destabilization using high energy milling. Journal of Non-Crystalline Solids, 2018, 480, pp.28-33. ⟨10.1016/j.jnoncrysol.2017.08.017⟩. ⟨hal-01660838⟩
193 Consultations
167 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More