Designing a Thermoelectric Copper-Rich Sulfide from a Natural Mineral: Synthetic Germanite Cu22Fe8Ge4S32 - Université de Rennes Access content directly
Journal Articles Inorganic Chemistry Year : 2017

Designing a Thermoelectric Copper-Rich Sulfide from a Natural Mineral: Synthetic Germanite Cu22Fe8Ge4S32

Abstract

This study shows that the design of copper-rich sulfides by mimicking natural minerals allows a new germanite-type sulfide Cu22Fe8Ge4S32 with promising thermoelectric properties to be synthesized. The Mössbauer spectroscopy and X-ray diffraction analyses provide evidence that the structure of our synthetic compound differs from that of the natural germanite mineral Cu26Fe4Ge4S32 by its much higher Cu(+)/Cu(2+) ratio and different cationic occupancies. The coupled substitution Cu/Fe in the Cu26-xFe4+xGe4S32 series also appears as a promising approach to optimize the thermoelectric properties. The electrical resistivity, which decreases slightly as the temperature increases, shows that these materials exhibit a semiconducting behavior, but are at the border of a metallic state. The magnitudes of the electrical resistivity and Seebeck coefficient increase with x, which suggests that Fe for Cu substitution decreases the hole concentration. The thermal conductivity decreases as the temperature increases leading to a moderately low value of 1.2 W m(-1) K(-1) and a maximum ZT value of 0.17 at 575 K.
Fichier principal
Vignette du fichier
Pavan Kumar - Designing a Thermoelectric Copper-Rich.pdf (1.54 Mo) Télécharger le fichier
Origin : Files produced by the author(s)
Loading...

Dates and versions

hal-01640116 , version 1 (01-02-2018)

Identifiers

Cite

Ventrapati Pavan Kumar, Laura Paradis-Fortin, P. Lemoine, Vincent Caignaert, Bernard Raveau, et al.. Designing a Thermoelectric Copper-Rich Sulfide from a Natural Mineral: Synthetic Germanite Cu22Fe8Ge4S32. Inorganic Chemistry, 2017, 56 (21), pp.13376-13381. ⟨10.1021/acs.inorgchem.7b02128⟩. ⟨hal-01640116⟩
279 View
293 Download

Altmetric

Share

Gmail Facebook X LinkedIn More