The forming region and mechanical properties of SiO2-Al2O3-MgO glasses

Ren Gao
  • Function : Author
Huanping Wang
  • Function : Correspondent author
Qingong Zhu
  • Function : Author
Qinghua Yang
  • Function : Author
Xingguo Sun
  • Function : Author
Bingpeng Li
  • Function : Author
Shiqing Xu
  • Function : Correspondent author
Xianghua Zhang

Abstract

The glasses of 93.9% (xSiO(2)-yAl(2)O(3)-zMgO)-5% CaO-1% B2O3-0.1% Fe2O3 were prepared, and the relationship between mechanical properties and structural stability were characterized by means of Raman spectroscopy and optical band gap values. The glass forming region is found to be x = 50-70%, y = 10-25% and z = 15-32%. As x = 65%, y = 10% and z = 25% (SAM-4), the investigated glass possesses the optimum volume density, oxygen packing density, optical band gap, banding strength, compression strength and compression modulus, which are 2.517 g/cm(3), 77.047 mol/l, 3.56 eV, 77.04 MPa, 202.74 MPa and 106.70 GPa, respectively. Meanwhile, starting from the representative point of SAM-4 to radiate around, the volume density, oxygen density, Raman intensity and mechanical properties of the glasses are all decreasing constantly, and the optical band gap of the glasses is increasing on the contrary. Moreover, the optical band gap value and Raman spectroscopy of SAM-4 all prove that the number of oxygen bonds in the bridge reach the maximum and the highest structural stability is achieved, which further shows that it is an important reason why its mechanical properties is significantly improved.
No file

Dates and versions

hal-01559203 , version 1 (10-07-2017)

Identifiers

Cite

Ren Gao, Huanping Wang, Qingong Zhu, Qinghua Yang, Xingguo Sun, et al.. The forming region and mechanical properties of SiO2-Al2O3-MgO glasses. Journal of Non-Crystalline Solids, 2017, 470, pp.132--137. ⟨10.1016/j.jnoncrysol.2017.05.004⟩. ⟨hal-01559203⟩
41 View
0 Download

Altmetric

Share

Gmail Facebook X LinkedIn More