Redox behaviour of potential SOFC cathode materials La1.6Sr0.4Ni1-​xCoxO4+δ (x = 0.6 and 0.8) determined from in situ neutron powder diffraction under flowing O2 and 5​%H2 - Université de Rennes Accéder directement au contenu
Article Dans Une Revue Key Engineering Materials Année : 2014

Redox behaviour of potential SOFC cathode materials La1.6Sr0.4Ni1-​xCoxO4+δ (x = 0.6 and 0.8) determined from in situ neutron powder diffraction under flowing O2 and 5​%H2

Domaines

Chimie
Fichier non déposé

Dates et versions

hal-01114491 , version 1 (09-02-2015)

Identifiants

Citer

James M. Hanlon, Florent Tonus, Thibault Broux, Carmelo Prestipino, Mona Bahout. Redox behaviour of potential SOFC cathode materials La1.6Sr0.4Ni1-​xCoxO4+δ (x = 0.6 and 0.8) determined from in situ neutron powder diffraction under flowing O2 and 5​%H2. Key Engineering Materials, 2014, 617, pp.89-93. ⟨10.4028/www.scientific.net/KEM.617.89⟩. ⟨hal-01114491⟩