Formation and properties of chalcogenide glasses based on GeS2-​Sb2S3-​AgI system

Résumé

Novel glasses in GeS2-​Sb2S3-​AgI system have been prepd. by melt-​quenching method. A large glass-​forming region was found in this novel system, in which almost 60 mol​% AgI has been incorporated. The basic physiochem. properties of glass samples were investigated. With the addn. of AgI, red shift of short-​wavelength absorption edge and distinct drop of the glass transition temp. (Tg) were obsd. In addn., a high Ag+ ion cond. of 6.37×10-​4 S​/cm at room temp. was obtained in 55(0.6GeS2-​0.4Sb2S3)​-​45AgI sample, indicating that these glasses have potential application as amorphous solid electrolytes.

Domaines

Matériaux
Fichier principal
Vignette du fichier
1-s2.0-S0167577X1401132X-main.pdf (502.45 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01058370 , version 1 (08-10-2014)

Identifiants

Citer

Zhuobin Li, Changgui Lin, Guoshun Qu, Laurent Calvez, Shixun Dai, et al.. Formation and properties of chalcogenide glasses based on GeS2-​Sb2S3-​AgI system. Materials Letters, 2014, 132, pp.203-205. ⟨10.1016/j.matlet.2014.06.083⟩. ⟨hal-01058370⟩
130 Consultations
437 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More