3D printed microchannel loaded with hematite nanoadsorbent for fluoride removal from water

Résumé

3D printed microchannels were loaded with α-Fe 2 O 3 nanoparticles for fluoride removal from water. Devices having 35 microchannels of 2 and 1.5 mm diameter were fabricated and loaded with 4 and 3 g of nanoadsorbent respectively. Hematite nanoadsorbent used shown good fluoride removal efficiency with a defluoridation capacity of 2.5 mg/g (3 mg/L fluoride concentration, 4 g adsorbent, 1 mL/min flow rate at 25 o C and 7 pH). The customized and compact 3D devices could be an alternative for traditional columns being used for effective fluoride removal from water.

Domaines

Chimie
Fichier principal
Vignette du fichier
Kumar Patel et al-2019-3D Printed Microchannel Loaded with Hematite Nanoadsorbent for Fluoride Removal.pdf (910.74 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02281769 , version 1 (14-10-2019)

Identifiants

Citer

R. Kumar Patel, A. Kumar Chawla, Patrick Loulergue, B. Teychene, J.K. Pandey. 3D printed microchannel loaded with hematite nanoadsorbent for fluoride removal from water. Materials Letters, 2019, 254, pp.190-193. ⟨10.1016/j.matlet.2019.07.061⟩. ⟨hal-02281769⟩
43 Consultations
171 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More