Nano structure Ti-doped skutterudite CoSb3 thin films through layer inter-diffusion for enhanced thermoelectric properties - Université de Rennes Accéder directement au contenu
Article Dans Une Revue Journal of the European Ceramic Society Année : 2019

Nano structure Ti-doped skutterudite CoSb3 thin films through layer inter-diffusion for enhanced thermoelectric properties

Zhuang-Hao Zheng
Connectez-vous pour contacter l'auteur
Fu Li
  • Fonction : Auteur
Hao Jin
  • Fonction : Auteur
Xianghua Zhang
Ping Fan
  • Fonction : Auteur

Résumé

Ti-doped CoSb3 thin films were prepared through layer inter-diffusion method and the prepared thin films have unique architecture, containing nano-size grains. According to the Raman analysis, the films have weaker atomic vibration after Ti doping. This nano-structure and the weak atomic vibration can scatter a wide-range spectrum of phonons, resulting the significantly decrease of thermal conductivity. In addition, this material design also leads to a very important improvement of the absolute Seeback coefficient value, which increases from about 50 VK-1 to over 100 VK-1. As the result, the maximum ZT value is 0.86 at 523 K for a Ti doped sample, which is six times higher than the un-doped sample and is comparable to the best value for the CoSb3 based thin films. A flexible CoSb3 based thin film thermoelectric generator was also fabricated and shows that the response time of all the touch events is below 1 s.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Liang et al-2019-Nano structure Ti-doped skutterudite CoSb3 thin films_accepted.pdf (1.36 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-02181828 , version 1 (18-10-2019)

Identifiants

Citer

Guang-Xing Liang, Zhuang-Hao Zheng, Fu Li, Jing-Ting Luo, Hao Jin, et al.. Nano structure Ti-doped skutterudite CoSb3 thin films through layer inter-diffusion for enhanced thermoelectric properties. Journal of the European Ceramic Society, 2019, 39 (15), pp.4842-4849. ⟨10.1016/j.jeurceramsoc.2019.06.044⟩. ⟨hal-02181828⟩
74 Consultations
128 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More