Stress release-induced interfacial twin boundary ω phase formation in a β type Ti-based single crystal displaying stress-induced α” martensitic transformation - Université de Rennes Accéder directement au contenu
Article Dans Une Revue Acta Materialia Année : 2018

Stress release-induced interfacial twin boundary ω phase formation in a β type Ti-based single crystal displaying stress-induced α” martensitic transformation

Résumé

The ω phase transformation in numerous group IV transition metals plays a key role to change the phase stability and modify mechanical properties, although its formation mechanisms and effect to accommodate strains are still unclear. A <1 1 0>β single crystal of β-type Ti-24Nb-4Zr-8Sn alloy (wt. %) is used to investigate the aforementioned problems. This alloy displays a β to α” stress-induced martensitic transformation, which is reversible and leads to superelasticity. Profiles obtained from in situ synchrotron X-ray diffraction during cyclic tensile tests reveal definitely the appearance of ω phase due to applied stress releasing after unloading while these identified ω peaks shall vanish totally on subsequent loading. TEM microstructural observations show its morphology as thin layer locating on the boundary of {1 1 2}<1 1 1>β twins coinciding well with the feature of interfacial twin boundary (ITB) ω phase, which is proved to be formed passively during the reversion of {1 1 0}<1 1 0>α” twins. The martensitic twinning components of {1 1 0}<1 1 0>α” are indeed confirmed from crystallographic reconstructions based on the orientation relationship between the β and α” phases. A geometrical model is hence schematically used to analyze in details the orientation relationships between both deformation {1 1 2}<1 1 1>β twins and ITB-ω phase, as well as with the original {1 1 0}<1 1 0>α” twinning.
Fichier principal
Vignette du fichier
Yang et al_Stress release-induced interfacial twin boundary ω phase formation in a β type.pdf (5.7 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01740146 , version 1 (06-07-2018)

Identifiants

Citer

Y. Yang, P. Castany, E. Bertrand, M. Cornen, J.X. Lin, et al.. Stress release-induced interfacial twin boundary ω phase formation in a β type Ti-based single crystal displaying stress-induced α” martensitic transformation. Acta Materialia, 2018, 149, pp.97-107. ⟨10.1016/j.actamat.2018.02.036⟩. ⟨hal-01740146⟩
152 Consultations
307 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More