A comparative study of structural and dielectric properties of diglycidyl ether of bisphenol A (DGEBA) cured with aromatic or aliphatic hardeners - Université de Rennes Accéder directement au contenu
Article Dans Une Revue Journal of Materials Science Année : 2016

A comparative study of structural and dielectric properties of diglycidyl ether of bisphenol A (DGEBA) cured with aromatic or aliphatic hardeners

Résumé

This study aims to present structural and dielectric comparisons between two epoxy polymers. These polymers are realized by curing diglycidyl ether of bisphenol A (DGEBA) resin with either aliphatic 1,3-diaminopropane (PDA) or aromatic 4,4′-diaminodiphenyl sulfone (DDS) hardeners. They are called DGEBA/PDA and DGEBA/DDS. Several complementary techniques have been used in the present study. The structural analysis was performed using grazing incidence X-ray reflectometry. It reveals the presence of a locally ordered nanostructure in the DGEBA/DDS polymer and an amorphous character for the DGEBA/PDA one. Dielectric characterization was carried by means of dielectric relaxation spectroscopy (DRS), thermally stimulated depolarization current (TSDC) and time domain spectroscopy (TDS). DRS measurements performed over wide ranges of temperature (−80 to 160 °C) and frequency (10−1–106 Hz) showed the presence of dipolar γ and α relaxations in both polymers. Nevertheless, the interfacial Maxwell–Wagner–Sillars (MWS) relaxation appeared only in DGEBA/DDS. This can be related to the local nanostructure within this polymer, which can give rise to interfaces. Relaxation parameters were deduced from the best fits of experimental data with the Havriliak–Negami model. The calculated fragility index indicates that DGEBA/DDS is more fragile than DGEBA/PDA. The loss factor ε′′(f) was calculated from the isothermal discharging current measurements, using Hamon approximation. Thanks to this ε′′ calculation an interfacial relaxation was revealed in the frequency range of 10−3–10−1 Hz for each investigated polymer.
Fichier non déposé

Dates et versions

hal-01679355 , version 1 (09-01-2018)

Identifiants

Citer

Wissal Jilani, Nissaf Mzabi, Najla Fourati, Chouki Zerrouki, Olivier Gallot-Lavallée, et al.. A comparative study of structural and dielectric properties of diglycidyl ether of bisphenol A (DGEBA) cured with aromatic or aliphatic hardeners. Journal of Materials Science, 2016, 51 (17), pp.7874 - 7886. ⟨10.1007/s10853-016-0043-0⟩. ⟨hal-01679355⟩
93 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More