A novel method determining longitudinally induced magnetic anisotropy in amorphous and nanocrystalline soft materials

Résumé

In ferromagnetic amorphous and nanocrystalline soft magnetic alloys the induced magnetic anisotropy plays a fundamental role in the hysteresis behavior but, due to the elongated shape, it can be measured only if $K_{U}$ is perpendicular to the sample long axis. In order to measure the longitudinal induced anisotropy, an original method derived from known thin layers measurement techniques was used. Hysteresis loops shifted by perpendicular bias field were recorded for this purpose. Direct measurement of the longitudinal induced anisotropy in amorphous and nanocrystalline ribbons or wire without needing sample preparation is reported for the first time. Evidence of self-induced anisotropy is brought in a Fe–Co-based nanocrystalline alloy.
Fichier principal
Vignette du fichier
Ku_meas_final4.pdf (167.66 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01496935 , version 1 (05-04-2017)

Identifiants

Citer

Frédéric Mazaleyrat, Zs Gercsi, Michel Lécrivain, L. K. Varga. A novel method determining longitudinally induced magnetic anisotropy in amorphous and nanocrystalline soft materials. Journal of Magnetism and Magnetic Materials, 2004, 280 (2-3), pp.391-394. ⟨10.1016/j.jmmm.2004.01.098⟩. ⟨hal-01496935⟩
164 Consultations
178 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More