Comparative Study of Nanobioactive Glass Quaternary System 46S6

Résumé

Different bioactive glass systems have been prepared by sol-gel. However, the production of Na2O-containing bioactive glasses by sol-gel methods has proved to be difficult as the sodium nitrate used in the preparation could be lost from the glass structure during filtration and washing. The aim of this study was to prepare the quaternary system 46S6 of bioactive glass by modified sol-gel techniques with a decrease in the time of gelation. In addition, compare the behaviour of the prepared sol-gel bioactive glass system by its corresponding prepared by melting. The obtained glasses were characterized by using several physicochemical techniques; XRD, FTIR, TEM and SEM beside the effect of the glass particles on the viability of osteoblast like cells (Saos-2). Results show that nanopowders 40-60 nm of 46S6 glass system had been prepared by modified sol-gel (acid-base reaction) method at 600°C in just three days at 600°C. Cell viability by MTT assay confirmed the effectiveness of the prepared nanobioactive glass.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Comparative_Study_of_Nanobioactive_Glass_Quaternary_System_46S6_accepted.pdf (1.36 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte
Loading...

Dates et versions

hal-01006548 , version 1 (16-06-2014)

Identifiants

Citer

Mostafa Mabrouk, Amany Mostafa, Hassane Oudadesse, Eric Wers, Anita Lucas-Girot, et al.. Comparative Study of Nanobioactive Glass Quaternary System 46S6. Bioceramics Development and Applications, 2014, 4 (1), pp.1000072. ⟨10.4172/2090-5025.1000072⟩. ⟨hal-01006548⟩
269 Consultations
258 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More