Electro-catalytic scission of carbon-iodine bonds. Building of SAMs at gold surfaces through long chain primary radical adsorption - Université de Rennes Accéder directement au contenu
Article Dans Une Revue Electrochemistry Communications Année : 2014

Electro-catalytic scission of carbon-iodine bonds. Building of SAMs at gold surfaces through long chain primary radical adsorption

Résumé

Primary alkyl iodides (RI) are reduced at smooth gold electrodes in polar organic solvents such as N,N-dimethylformamide (DMF) in the presence of tetraalkylammonium salts (TAAX). Beside a main two-electron step currently observed at potential > − 2.0 V vs. Ag/AgCl, a bell-shaped step appears with all organic iodides within a potential range between − 0.6 V and − 1.2 V. This peak does not depend on the organic substrate concentration, its current is proportional to the scan rate in voltammetry; it disappears at the second scan. These features arise from slow adsorption of the RI at gold, followed by an electro-catalytic reduction induced by the metal. It is expected that this (simple) process allows the formation of alkyl radicals readily adsorbed at the metal surface and thus produced layer strongly inhibits the main cathodic step at more negative potentials. With linear chains in C10, C12, C16 and C18, the coverage of gold leads to self-assembled monolayers (SAMs). The compactness of this coverage was found to be about 10− 10 mol cm− 2.
Fichier principal
Vignette du fichier
Electro-catalytic_Scission_of_Carbon-Iodine_Bonds-accepted.pdf (382.13 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-00977510 , version 1 (11-04-2014)

Identifiants

Citer

Jacques Simonet, Viatcheslav Jouikov. Electro-catalytic scission of carbon-iodine bonds. Building of SAMs at gold surfaces through long chain primary radical adsorption. Electrochemistry Communications, 2014, 38, pp.65-67. ⟨10.1016/j.elecom.2013.11.003⟩. ⟨hal-00977510⟩
117 Consultations
158 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More