Reactive Sputtering Deposition of Perovskite Oxide and Oxynitride Lanthanum Titanium Films: Structural and Dielectric Characterization - Université de Rennes Accéder directement au contenu
Article Dans Une Revue Crystal Growth & Design Année : 2013

Reactive Sputtering Deposition of Perovskite Oxide and Oxynitride Lanthanum Titanium Films: Structural and Dielectric Characterization

Stéphane Rioual

Résumé

Perovskite lanthanum titanium thin films were deposited on Nb-doped (001) SrTiO3 substrates by reactive RF magnetron sputtering using a La2Ti2O7 target. Oxynitride LaTiO2N films were obtained using N2 rich plasma; they display a variation of their dielectric constant as a function of DC bias in the low frequency range but not in microwaves. The dielectric constant (epsilon) values are high with, for example, epsilon = 325 at 100 kHz. The oxide films, obtained in O2 rich plasma, are composed of an unusual La2Ti2O7 phase with an orthorhombic cell. The films are (101) epitaxied on Nb:SrTiO3 substrates. The dielectric constant value of films is around 77 with losses 0.076 at 100 kHz; no agility of epsilon in low and high frequencies is detected. Composite and bilayer films, with oxynitride and oxide phases, exhibit a variation of epsilon under DC bias in low frequencies with, for example, an agility of 15% at 100 kHz with a maximum applied field of 40 kV/cm for the LaTiO2N (200 nm)/La2Ti2O7 (250 nm) bilayer.

Domaines

Matériaux
Fichier non déposé

Dates et versions

hal-00875068 , version 1 (21-10-2013)

Identifiants

Citer

Yu Lu, Claire Le Paven-Thivet, Hung Nguyen, Ratiba Benzerga, Laurent Le Gendre, et al.. Reactive Sputtering Deposition of Perovskite Oxide and Oxynitride Lanthanum Titanium Films: Structural and Dielectric Characterization. Crystal Growth & Design, 2013, pp.4852-4858. ⟨10.1021/cg4010196⟩. ⟨hal-00875068⟩