Glass Formation and Crystallization Behavior of a Novel GeS2-Sb2S3-PbS Chalcogenide Glass System

Fang Xia
  • Fonction : Auteur
Xianghua Zhang
Jing Ren
  • Fonction : Auteur
Guorong Chen
  • Fonction : Auteur correspondant
  • PersonId : 945409

Connectez-vous pour contacter l'auteur
Hongli Ma
Jean-Luc Adam

Résumé

In the present work, a large glass-forming region was found in the novel GeS2-Sb2S3-PbS system, in which up to 58 at.% PbS could be incorporated without deteriorating the thermal and physical properties of glasses. Infrared (IR) transmitting glass ceramics with a large amount of small-sized crystals (<100 nm) were then produced by choosing sub-stable compositions and annealing at fairly low temperatures (15°-30°C above Tg) for long durations (up to 100 h). Crystals were identified by X-ray diffraction as Pb2GeS4, PbGeS3, PbS, PbSb2S4, etc., depending on base glass compositions. Compared with base glasses, glass ceramics showed much improved thermal shock resistance and fracture toughness, making them good candidate materials for IR optics.

Domaines

Matériaux

Dates et versions

hal-00866974 , version 1 (27-09-2013)

Identifiants

Citer

Fang Xia, Xianghua Zhang, Jing Ren, Guorong Chen, Hongli Ma, et al.. Glass Formation and Crystallization Behavior of a Novel GeS2-Sb2S3-PbS Chalcogenide Glass System. Journal of the American Ceramic Society, 2006, 89 (7), pp.2154-2157. ⟨10.1111/j.1551-2916.2006.01058.x⟩. ⟨hal-00866974⟩
186 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More