Effects of cold-rolling deformation on texture evolution and mechanical properties of Ti-29Nb-9Ta-10Zr alloy
Résumé
The crystallographic texture of Ti-29Nb-9Ta-10Zr alloy is studied after cold-rolling with different amounts of thickness reduction, up to 60%. The major texture components developed during cold-rolling were: γ-fibre components: {111}〈View the MathML source〉, {111}〈View the MathML source〉, {111}〈View the MathML source〉 and {111}〈View the MathML source〉; texture component: {112}〈View the MathML source〉 and texture components: {001}〈View the MathML source〉 and {010}〈001〉. Besides crystallographic texture the resulted mechanical properties were studied by nanoindentation. It was showed that the decrease in Young's modulus after different cold-rolling stages is mainly attributed to the stress-induced α″-Ti phase formation. At 60% cold-rolling thickness reduction obtained an elastic modulus close to 45.29±3.81 GPa, coupled with an average Vickers microhardness close to 279.83±4.28 HV.
Domaines
Génie chimique
Origine : Fichiers produits par l'(les) auteur(s)
Loading...