SiGe derivatization by spontaneous reduction of aryl diazonium salts - Université de Rennes Accéder directement au contenu
Article Dans Une Revue Applied Surface Science Année : 2013

SiGe derivatization by spontaneous reduction of aryl diazonium salts

Résumé

Germanium semiconductors have interesting properties for FET-based biosensor applications since they possess high surface roughness allowing the immobilization of a high amount of receptors on a small surface area. Since SiGe combined low cost of Si and intrinsic properties of Ge with high mobility carriers, we focused the study on this particularly interesting material. The comparison of the efficiency of a functionalization process involving the spontaneous reduction of diazonium salts is studied on Si(1 0 0), SiGe and Ge semiconductors. XPS analysis of the functionalized surfaces reveals the presence of a covalent grafted layer on all the substrates that was confirmed by AFM. Interestingly, the modified Ge derivatives have still higher surface roughness after derivatization. To support the estimated thickness by XPS, a step measurement of the organic layers is done by AFM or by profilometer technique after a O2 plasma etching of the functionalized layer. This original method is well-adapted to measure the thickness of thin organic films on rough substrates such as germanium. The analyses show a higher chemical grafting on SiGe substrates compared with Si and Ge semiconductors.

Domaines

Autre
Fichier principal
Vignette du fichier
SiGe-derivatization-postprint-accepted.pdf (9.53 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-00860238 , version 1 (10-09-2013)

Identifiants

Citer

Aurélie Girard, Florence Geneste, Nathalie . Coulon, Christophe Cardinaud, Tayeb Mohammed-Brahim. SiGe derivatization by spontaneous reduction of aryl diazonium salts. Applied Surface Science, 2013, 282, pp.146-155. ⟨10.1016/j.apsusc.2013.05.091⟩. ⟨hal-00860238⟩
457 Consultations
287 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More