Hard magnetic properties of melt-spun Mn-Al-C alloys - Université de Rennes Accéder directement au contenu
Article Dans Une Revue EPJ Web of Conferences Année : 2013

Hard magnetic properties of melt-spun Mn-Al-C alloys

Résumé

Structural and magnetic characterization of Mn(x−y)Al(100−x−y)C(2y) (x = {50, 55}; y = {0, 1}) melt-spun ribbons is reported. To obtain the metastable ferromagnetic τ-phase, rapidly solidified alloys were annealed either in a vacuum furnace at 823 K or directly in the vibrating sample magnetometer under applied magnetic field. Optimal magnetic properties were demonstrated by Mn54Al44C2 samples proved to be single-phase with a coercivity of 0.19 T measured in both cases. For this composition the structural ε→τ phase transformation has been magnetically detected at 786 K, Curie temperature of τ-phase (Tc = 592 K, Tp = 610 K) has been determined using mean field approximations in ferromagnetic and paramagnetic regions. Rietveld refinement of X-ray diffraction spectra was employed to analyse the phase constitution of annealed alloys, lattice parameters as a function of chemical composition and mean grain size for the phases involved.
Fichier principal
Vignette du fichier
jems2012_pasko.pdf (716.94 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-00827620 , version 1 (29-05-2013)

Identifiants

Citer

Alexandre Pasko, Frederic Mazaleyrat, Martino Lobue, E. Fazakas, L. K. Varga. Hard magnetic properties of melt-spun Mn-Al-C alloys. EPJ Web of Conferences, 2013, 40, pp.06008. ⟨10.1051/epjconf/20134006008⟩. ⟨hal-00827620⟩
179 Consultations
161 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More