Luminescence behavior of Er3+ doped glass ceramics containing Sr2RF7 (R=Y, Gd, La) nanocrystals

Résumé

The luminescence behaviors of Er3+ doped glass ceramics containing Sr2RF7 (R = Y,Gd,La) nanocrystals were investigated. The formation of Sr2RF7 nanocrystals in the glass ceramics was confirmed by x-ray diffraction and high resolution transmission electron microscopy. Energy dispersive x-ray spectroscopy analysis showed that the Er3+ ions were efficiently incorporated in Sr2GdF7 nanocrystals. The efficient upconversion luminescence of the Er3+ in the glass ceramics can be observed. The lifetime of the Er3+ in the glass ceramics was found to be much longer than that in the glass due to the lower phonon energy of fluoride crystals when Er3+ entered efficiently fluoride crystals in the glass ceramics.

Dates et versions

hal-00402224 , version 1 (07-07-2009)

Identifiants

Citer

Xvsheng Qiao, Xianping Fan, Minquan Wang, Hui Yang, Xianghua Zhang. Luminescence behavior of Er3+ doped glass ceramics containing Sr2RF7 (R=Y, Gd, La) nanocrystals. Journal of Applied Physics, 2008, 104 (4), pp.043508. ⟨10.1063/1.2969039⟩. ⟨hal-00402224⟩
68 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More